Specifications
Powder
| Grade | TiO2Crystal structure | TiO2(%) | TiO2Crystal size(nm) | pH | Specific surface area(m2/g) | Product feature |
|---|---|---|---|---|---|---|
| AMT-100 | Anatase | 93 | 6 | Neutral | 280 | large specific surface area,suitable gas decomposition |
| AMT-600 | 98 | 30 | Slightly acidic | 52 | easily dispersion in medium for general usage | |
| TITANIX JA-1 | 99 | 180 | Neutral | 9 | pigmentary grade | |
| TKP-101 | 83 | 6 | Slightly acidic | 300 | for ammonia gas decomposition | |
| TKP-102 | 96 | 15 | Slightly acidic | 110 | for aldehyde gas decomposition |
Titania sol
| Grade | TiO2Crystal structure | TiO2(%) | TiO2Crystal size(nm) | pH | medium | Product feature |
|---|---|---|---|---|---|---|
| TKS-201 | Anatase | 33 | 6 | Acidic | Water | stabilizer：HCl |
| TKS-202 | 33 | 6 | Acidic | Water | stabilizer：HNO3 | |
| TKS-203 | 20 | 6 | Neutral | Water | neutral Titania sol |
- * have excellent dispersion stability under dilution by own medium.
- * have excellent storage stability.
Slurry
| Grade | TiO2Crystal structure | TiO2(%) | TiO2Crystal size(nm) | pH | Specific surface area(m2/g) | Product feature |
|---|---|---|---|---|---|---|
| TKD-701 | Anatase | 17 | 6 | – | IPA | using AMT-100 |
| TKD-702 | 16 | 6 | – | IPA | using TKP-101 | |
| TKD-801 | 17 | 6 | Neutral | Water | using AMT-100 | |
| TKD-802 | 16 | 6 | Neutral | Water | using TKP-101 |
- * have excellent dispersibility.
Titania coatings
| Grade | TiO2Crystal structure | N.V.(%) | TiO2Crystal size(nm) | pH | medium | Product feature |
|---|---|---|---|---|---|---|
| TKC-303 | Anatase | 13 | 6 | Acidic | Water | high TiO2 concentration, and can harden at room temp, and exhibit high photocatalytic activity and high film hardness. |
| TKC-304 | Anatase | 9 | 6 | Neutral | Water | neutral and high TiO2 concentration, and can harden at room temp, and exhibit high photocatalytic activity and high film hardness. |
| TKC-305 | Amorphous | 5*1 | – | Slightly acidic | Water | Titanyl Ammonium Oxalate can exhibit very high film hardness by calcination(500℃). |
- * can make transparent film.
- * medium is water,and TKC-304 is neutral,so they are adaptable to many substrate.
- * adaptable to all coating system(ex:Coater,spray,dip.spin,blush)
- *1 Residue on ignition at 500℃