Specifications | Aluminium triphosphate | Product

[ K-WHITE ]

#82	White powder	0.9	0.3	6.5	38	3.0	3.9	3.5
#84	White powder	0.8	0.3	6.4	33	3.1	3.4	3.7
#84S	White powder	0.9	0.2	6.5	31	2.9	3.3	3.7
#85	White powder	0.8	0.1	6.6	27	3.3	3.6	3.7
#105	White powder	0.8	0.3	6.5	33	3.0	3.1	1.6
#140W	White powder	1.0	1.0	7.0	37	3.0	4.0	2.7
G105	White powder	1.5	1.2	9.5	40	2.6	4.3	2.3
#450H	White powder	4.1	3.7	7.7	53	2.2	4.1	3.5
Ca650	White powder	1.0	2.2	7.1	36	2.5	4.6	3.5
#94	White powder	0.4*⁴	0.3	6.8	34	2.9	3.4	6.3

Representative analysis

*1 JIS K5101 drying temperature at 90±1 degrees Centigrade
*2 JIS K5101 kerosene substituted with water
*3 Equipment: Coulter Multisizer (manufactured by Nikkaki)
Measuring conditions: measured after 5 minutes of ultrasonic dispersion in 0.1% sodium hexametaphosphate solution.
*4 JIS K5101 drying temperature at 180 degrees Centigrade

[ K-BOND ]

#80	White powder	4.3	0.5	1.4	2.4	Short
#90	White powder	1.7	0.3	1.3	2.9	Long

Representative analysis

*1 0.5 g of sample in a 100-ml beaker is added with 30 ml of 0.1 N-KOH and pure water to produce a mixture of 50 ml. Then, the mixture is agitated for about 2 hours.

W:Sample weight(g) V:0.1 N-HCL titer(ml)
*2 JIS K5101 drying temperature at 90±1 degrees Centigrade
*3 Water-glass-based relative comparison

[ K-FRESH ]

#100P	White powder	0.9	3.0	◎	◎	×	×	×	×
MZO	White powder	0.2	7.4	×	×	◎	◎	×	×
ZA	White powder	2.0	7.6	×	×	×	×	◎	◎

Representative analysis

Adsorbency:◎…Very high ○…High ×…Almost none
*1 JIS K5101 drying temperature at 90±1 degrees Centigrade
*2 5% turbidity solution at room temperature used for measurement